907 Suhu Tinggi Novolac Resin Swancor 907 Chempulse

907 Suhu Tinggi Novolac Resin Swancor 907 Chempulse

$3≥1000Others

Jenis pembayaran:	L/C,Western Union,T/T
Min. Memesan:	1000 kilogram
Pelabuhan:	Shanghai Port of China

Hubungi sekarang

Deskripsi Produk

Atribut Produk

& pengiriman paket

Deskripsi Produk

Atribut Produk

CAS No.: un-available

Other Names: VE resin

MF: un-available

EINECS No.: un-available

Type: Synthetic Resin And Plastics

Brand Name: Swancor

Model Number: 907

Appearance: Light yellow transparent liquid

Density: 1.06±0.02kg/L

Viscosity: 430±150 cps (LVT#3-60rpm/25℃)

Solid Content: 62±1.5%

Gel Time: 15-25min

Storage Period: 4 month(below 25℃)

Manufacturing Process: filament winding or spray up process

Feature: high distortion temperature

Aplikasi: high-temperature flue and smoke pipe

Waktu pengiriman: 20 days after deposit in account

Place Of Origin: Jiangsu, China

Purity: 55%

& pengiriman paket

Menjual unit	:	kilogram
Tipe paket	:	dikemas dalam kotak plastik, 20kg/drum
Contoh pada gamba	:

The file is encrypted. Please fill in the following information to continue accessing it

Suhu Tinggi Novolac Resin Swancor 907 Chempulse1



Deskripsi Produk

Novolac Epoxy Vinyl Ester Resin

1. Sifat mekanik surperior dan ketahanan kimia pada suhu tinggi.
2. Suhu distorsi panas tinggi
3. Dengan resistensi fatique yang sangat baik.
4. Cocok untuk aplikasi korosif yang lebih agresif.

5. Warna casting yang lebih rendah

Penampilan Produk

Penampilan

Paket 20kg/drum

Properti tubuh casting resin poliester

Appearance	light yellow transparent liquid
Density	1.06±0.02kg/L
Viscosity	430±150 cps (LVT#3-60rpm/25℃)
Solid content	62±1.5%
Gel time	15-25min (55%MEKPO：1.2%，6% cobalt Octoate 0.4%，100%DMA：0.05%，temperature：25℃ water bath)
Storage period	4 month(below 25℃)

Lembar data Produk

Item	Data	Test method
Tensile strength	76-90MPa	ASTM D 638
Tensile modulus	3.4-3.7GPa	ASTM D 638
Elongation	2.5-4.0%	ASTM D 638
Bending strength	124-145MPa	ASTM D 790
Bending modulus	3.7-4.1GPa	ASTM D 638
Distortion temperature	144-150℃	ASTM D 638
Hardness	40-46 Barcol	ASTM D 2583

Aplikasi

Tangki penyimpanan asam klorida (HCl)

Kimia: 31% HCl, Suhu 60 ℃ Resin Vinyl Digunakan: Swancor Chempulse 907

Proses pembuatan: Semprotkan lapisan

Aplikasi Swancor 907

Produk SWANCOR 907 Series adalah resin ester vinil epoksi fenolik dengan kepadatan ikatan silang tinggi dan ketahanan panas yang baik (The
Suhu distorsi panas dapat mencapai 150 ℃ atau bahkan lebih tinggi), terutama untuk larutan yang mengandung klorin atau pelarut organik. Dia
dapat digunakan dalam beberapa kesempatan di mana suhunya relatif tinggi, seperti persiapan buang suhu tinggi dan asap
pipa, dan di industri klor-alkali, industri pembuatan kertas, penyimpanan minyak dan gas, industri elektroplating, peleburan logam
Industri, dll juga banyak digunakan.

Kemasan